Stud link anchor chain
STUD LINK ANCHOR CHAIN ABS LRS DNVGL BV NKK CCS RMRS IRS CCS RINA KR APPROVAL Material(Grade): U1:Q235 U2:CM490 U3:CM690 Surface treatment: Self color, Paint coating,Hot Dip Galvanizing
| Chain diameter | Grade U1 | Grade U2 | Grade U3 | |||
| mm | Proof load | Breaking load | Proof load | Breaking load | Proof load | Breaking load |
| 12,5 | 46 | 66 | 66 | 92 | — | — |
| 14 | 58 | 82 | 82 | 115 | — | — |
| 16 | 75 | 107 | 107 | 150 | — | — |
| 17,5 | 89 | 128 | 128 | 179 | — | — |
| 19 | 105 | 150 | 150 | 211 | — | — |
| 20,5 | 122 | 175 | 175 | 244 | 244 | 349 |
| 22 | 140 | 201 | 201 | 281 | 281 | 401 |
| 24 | 166 | 238 | 238 | 333 | 333 | 475 |
| 26 | 194 | 278 | 278 | 389 | 389 | 556 |
| 28 | 225 | 321 | 321 | 450 | 450 | 642 |
| 30 | 257 | 367 | 367 | 514 | 514 | 734 |
| 32 | 291 | 416 | 416 | 583 | 583 | 832 |
| 34 | 327 | 468 | 468 | 655 | 655 | 936 |
| 36 | 366 | 523 | 523 | 732 | 732 | 1045 |
| 38 | 406 | 580 | 580 | 812 | 812 | 1160 |
| 40 | 448 | 640 | 640 | 896 | 896 | 1280 |
| 42 | 492 | 703 | 703 | 984 | 984 | 1406 |
| 44 | 538 | 769 | 769 | 1076 | 1076 | 1537 |
| 46 | 585 | 837 | 837 | 1171 | 1171 | 1673 |
| 48 | 635 | 908 | 908 | 1270 | 1270 | 1814 |
| 50 | 686 | 981 | 981 | 1373 | 1373 | 1961 |
| 52 | 739 | 1057 | 1057 | 1479 | 1479 | 2113 |
| 54 | 794 | 1135 | 1135 | 1589 | 1589 | 2269 |
| 56 | 850 | 1216 | 1216 | 1702 | 1702 | 2430 |
| 58 | 908 | 1299 | 1299 | 1818 | 1818 | 2597 |
| 60 | 968 | 1384 | 1384 | 1938 | 1938 | 2767 |
| 62 | 1029 | 1472 | 1472 | 2060 | 2060 | 2943 |
| 64 | 1092 | 1562 | 1562 | 2187 | 2187 | 3123 |
| 66 | 1157 | 1655 | 1655 | 2316 | 2316 | 3308 |
| 68 | 1223 | 1749 | 1749 | 2448 | 2448 | 3496 |
| 70 | 1291 | 1846 | 1846 | 2583 | 2583 | 3690 |
| 73 | 1395 | 1995 | 1995 | 2792 | 2792 | 3988 |
| 76 | 1503 | 2149 | 2149 | 3007 | 3007 | 4295 |
| 78 | 1576 | 2254 | 2254 | 3154 | 3154 | 4505 |
| 81 | 1689 | 2415 | 2415 | 3380 | 3380 | 4827 |
| 84 | 1805 | 2580 | 2580 | 3612 | 3612 | 5158 |
| 87 | 1923 | 2750 | 2750 | 3849 | 3849 | 5498 |
| 90 | 2045 | 2924 | 2924 | 4093 | 4093 | 5845 |
| 92 | 2127 | 3042 | 3042 | 4258 | 4258 | 6081 |
| 95 | 2254 | 3223 | 3223 | 4510 | 4510 | 6442 |
| 97 | 2339 | 3345 | 3345 | 4682 | 4682 | 6687 |
| 100 | 2470 | 3532 | 3532 | 4943 | 4943 | 7060 |
| 102 | 2558 | 3658 | 3658 | 5120 | 5120 | 7312 |
| 105 | 2692 | 3850 | 3850 | 5389 | 5389 | 7697 |
| 107 | 2783 | 3980 | 3980 | 5571 | 5571 | 7957 |
| 111 | 2968 | 4245 | 4245 | 5941 | 5941 | 8486 |
| 114 | 3110 | 4447 | 4447 | 6224 | 6224 | 8889 |
| 117 | 3253 | 4652 | 4652 | 6511 | 6511 | 9299 |
| 120 | 3398 | 4859 | 4859 | 6801 | 6801 | 9714 |
| 122 | 3496 | 4999 | 4999 | 6997 | 6997 | 9994 |
| 124 | 3595 | 5141 | 5141 | 7195 | 7195 | 10276 |
| 127 | 3744 | 5354 | 5354 | 7494 | 7494 | 10703 |
| 130 | 3895 | 5571 | 5571 | 7796 | 7796 | 11135 |
| 132 | 3997 | 5716 | 5716 | 8000 | 8000 | 11426 |
| 137 | 4254 | 6083 | 6083 | 8514 | 8514 | 12161 |
| 142 | 4515 | 6456 | 6456 | 9036 | 9036 | 12906 |
| 147 | 4779 | 6834 | 6834 | 9565 | 9565 | 13662 |
| 152 | 5046 | 7217 | 7217 | 10100 | 10100 | 14426 |
| 157 | 5316 | 7602 | 7602 | 10640 | 10640 | 15197 |
| 162 | 5588 | 7991 | 7991 | 11185 | 11185 | 15975 |
Grade | Chemical composition of butt welded and forged anchor chain Chemical composition % | ||||||||||||
C | Si | Mn | P | S | Al | N | Cr | Cu | Nb | Ni | V | Mo | |
max. | max. | max. | max. | max. | max. | max. | max. | max. | max. | ||||
U1 | 0,20 | 0,15 – 0,35 | 0,40 min. | 0,04 | 0,04 | — | — | — | — | — | — | — | — |
U2 | 0,24 | 0,15 – 0,55 | 1,60 max. | 0,035 | 0,035 | 0,02 min. see Note 1 | — | — | — | — | — | — | — |
U3 | 0,33 | 0,15 – 0,35 | 1,90 max. | 0,04 | 0,04 | 0,065 max. see Note 2 | 0,015 | 0,25 | 0,35 | 0,05 see Note 2 | 0,40 | 0,10 see Note 2 | 0,08 |
NOTES 1. Aluminium may be partly replaced by other grain refining elements. 2. To obtain fine grain steel, at least one of these grain refining elements must be present in sufficient amount. | |||||||||||||